A514 Gr C Steel Plate A514 Hot Rolled Steel Sheet High Strength High Tensile Astm A514 Steel Plate
A514 is a quenched and tempered high strength weldable steel plate under ASTM standards. ASTM A514steel plate is characterized by high strength and good weldability.
| Product Name | A514 Gr.C Low Alloy High Strength Steel Plate |
| Material | A514 Gr.C |
| Standard | AISI, ASTM, BS, DIN, GB, JIS |
| Technique | Hot rolled |
| Surface Treatment | Coated or as Customers' Request |
| Package | Outer Packing: Export Standard Packing Method(Waterproof packing, Bundle with steel strip, Steel pallet), Shipped with 20' or 40' container or in bulk carrier. As Customers' Request. |
| Port | Shanghai,Tian jin, Qingdao or as required |
| Date of delivery | 15-30 days after deposit received or L/C received in our bank |
A514 G rade C Chemical Composition Max (%)
| Element | A514 Grade A | A514 Grade B | A514 Grade C | A514 Grade E | A514 Grade F | A514 Grade H | A514 Grade J |
| C | 0.15-0.21 | 0.12-0.21 | 0.1-0.2 | 0.12-0.20 | 0.1-0.2 | 0.12-0.21 | 0.12-0.21 |
| M | 0.80-1.10 | 0.70-1.0 | 1.10-1.5 | 0.4-0.7 | 0.60-1.0 | 0.95-1.3 | 0.45-0.7 |
| P | 0.035 | 0.035 | 0.035 | 0.035 | 0.035 | 0.035 | 0.035 |
| S | 0.035 | 0.035 | 0.035 | 0.035 | 0.035 | 0.035 | 0.035 |
| Si | 0.4-0.8 | 0.20-0.35 | 0.15-0.30 | 0.2-0.4 | 0.15-0.35 | 0.20-0.35 | 0.20-0.35 |
| Ni | - | - | - | - | 0.70-1.0 | 0.3-0.7 | - |
| Cr | 0.5-0.8 | 0.4-0.65 | - | 1.40-2.0 | 0.4-0.65 | 0.4-0.65 | - |
| Mo | 0.18-0.28 | 0.15-0.25 | 0.15-0.30 | 0.4-0.6 | 0.4-0.6 | 0.2-0.3 | 0.50-0.65 |
| V | - | 0.03-0.08 | - | - | 0.03-0.08 | 0.03-0.08 | - |
| Ti | - | 0.01-0.03 | - | 0.01-0.10 | - | - | - |
| Z | 0.05-0.15 | - | - | - | - | - | |
| Cu | - | - | - | 0.15-0.50 | 0.15-0.50 | - | - |
| B | 0.0025 | 0.001-0.005 | 0.001-0.005 | 0.001-0.005 | 0.001-0.005 | 0.001-0.005 | 0.001-0.005 |
| Nb | - | - | - | - | - | - | - |
A514 Grade C Mechanical Property
| Grade | Thickness | Yield | Tensile | Elongation |
| A514 grade C | mm | Min Mpa | Mpa | Min % |
| 20 | 690 | 760-895 | 18 | |
| 20-65 | 690 | 760-895 | 18 | |
| 65-150 | 620 | 690-895 | 18 |
What is the heat treatment for A514 steel?
Heat treatment of ASTM A514 Steel Plate In order to meet the tensile and Brinell hardness requirements specified in Table 2, the steel plates shall be heat treated, that is, the steel plates shall be heated to not less than 1650°F (900°C), quenched in water or oil, and not less than 1150°F (620°C) fire
Suitable for wide variety of structural application for instance: freight cars, transmission towers, dump trucks, cranes, trailers, bull dozers, excavators, forestry machines, railway wagons, dolphins, penstocks, pipes, highway bridges, building structures, offshore structures, shipbuilding, fans, pumps, lifting equipments and port equipments.