NM400 NM450 NM500 Wearing Resistant Steel Plate Abrex 500 High Strength Wear Steel
NM500 Steel is a steel grade specified in the Chinese national standard GB 24186. NM 500 steel is recognized for its exceptional hardness and durability, making it a high-strength, wear-resistant, and abrasion-resistant steel.
Product Specifications
| Product Name |
Wholesale Price Wear Steel Plate Hardness 500 Wear Nm500 Nm600 Plate Wear Plate Used For Thermal Power Plant |
| GB |
NM300, NM360, NM400, NM450, NM500 |
| DIN |
XAR400, XAR450, XAR500, XAR600, Dillidur400, Dillidur500 |
| NBN |
QUARD400, QUARD450, QUARD500 |
| NF |
FORA400, FORA500, Creusabro4800, Creusabro8000 |
| JIS |
JFE-EH360, JFE-EH400, JFE-EH500, WEL-HARD400, WEL-HARD500 |
Key Features
-
High wear resistance: The wear resistance is significantly higher than ordinary steel plates, with a 15-20 times increase compared to ordinary steel, 5-10 times increase compared to low-alloy steel plates, and 2-5 times increase compared to high-chromium cast iron.
-
Better impact performance: The wear-resistant layer effectively withstands wear from the medium, while the substrate carries the load of the medium.
-
Better heat resistance: The alloy wear-resistant layer is best used at temperatures ≤600ºC. By adding vanadium, molybdenum, and other alloys, it can endure high-temperature wear of up to ≤800ºC.
-
Good corrosion resistance: The alloy layer contains a high concentration of metallic chromium, providing decent rust and corrosion resistance.
-
Good processing performance: The wear-resistant steel plate can be easily cut, bent, crimped, welded, punched, and formed into various parts.
Technical Parameters
NM500 Chemical Composition
| Grade |
C |
Si |
Mn |
P |
S |
Cr |
Ni |
Mo |
Ti |
B |
Al |
| NM500 |
≤0.38 |
≤0.70 |
≤1.70 |
≤0.020 |
≤0.010 |
≤1.50 |
≤1.00 |
≤0.65 |
≤0.50 |
0.0005-0.006 |
≥0.01 |
NM500 Steel Properties
NM500 steel exhibits excellent wear resistance due to its high hardness level.
Mechanical Properties of NM 500
| Grade |
Mechanical Property |
| NM 500 |
Tensile: 1350 Mpa |
| Elongation: Min 7% |
Charpy V Impact Test
| NM500 |
Thickness |
Hardness (HB) |
|
≤70mm |
420~480 |
| >70~100mm |
450~540 |
Applications
It can be cut, bent, welded, and more, allowing for easy connection with other structures through methods like welding, plug welding, bolting, among others. This versatility saves time during repair work on-site.
This material finds extensive applications in various industries including metallurgy, coal, cement, electricity, glass, mining, building materials, bricks, and tiles. With its high cost-effectiveness compared to alternative materials, it is gaining increasing popularity among industries and manufacturers.
Frequently Asked Questions
Q: What is the brand name of the High Strength Steel Plate?
A: The brand name is GNEE.
Q: What are the model numbers available for the High Strength Steel Plate?
A: The available model numbers are NM360, NM400, NM450, NM500, NM550, and NM600.
Q: Where is the High Strength Steel Plate manufactured?
A: The High Strength Steel Plate is manufactured in China.
Q: What are the main features of the High Strength Steel Plate?
A: The High Strength Steel Plate offers exceptional durability and resistance to wear and tear, making it ideal for heavy-duty applications.
Q: Can the High Strength Steel Plate be customized in terms of size and thickness?
A: Yes, the High Strength Steel Plate can be customized to meet specific size and thickness requirements based on the customer's needs.